VALOX ENH4560 30%玻璃纤维增强的注塑级树脂
参数
  • 否是否进口
  • 中国厂家(产地)
  • ENH4560 牌号
广东 东莞 不限
东莞市聚浩塑化有限公司 2年
进入店铺 在线咨询
产品详情

PROPERTIES
TYPICAL VALUESUNITSTEST METHODS
FLAME CHARACTERISTICS1)


UL Yellow Card Link
E45329-100522223--
UL Yellow Card Link 2
E45329-104546523--
UL Recognized, 94-5VB Flame Class Rating
≥1.5mmUL 94
UL Recognized, 94-5VA Flame Class Rating
≥1.5mmUL 94
Glow Wire Ignitability Temperature, 3.0 mm
800°CIEC 60695-2-13
UL Recognized, 94V-0 Flame Class Rating
≥0.8mmUL 94
Glow Wire Ignitability Temperature, 2.0 mm
750°CIEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm
775°CIEC 60695-2-13
Glow Wire Ignitability Temperature, 1.0 mm
750°CIEC 60695-2-13
Glow Wire Ignitability Temperature, 0.8 mm
750°CIEC 60695-2-13
Glow Wire Flammability Index, 3.0 mm
960°CIEC 60695-2-12
Glow Wire Flammability Index, 2.0 mm
960°CIEC 60695-2-12
Glow Wire Flammability Index, 1.5 mm
960°CIEC 60695-2-12
Glow Wire Flammability Index, 1.0 mm
960°CIEC 60695-2-12
Glow Wire Flammability Index, 0.8 mm
960°CIEC 60695-2-12
UV-light, water exposure/immersion
F1-UL 746C
MECHANICAL2)


Tensile Stress, yld, Type I, 5 mm/min
105MPaASTM D638
Tensile Stress, brk, Type I, 5 mm/min
105MPaASTM D638
Tensile Strain, yld, Type I, 5 mm/min
2%ASTM D638
Tensile Strain, brk, Type I, 5 mm/min
2%ASTM D638
Tensile Modulus, 5 mm/min
11000MPaASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span
160MPaASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span
160MPaASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span
9300MPaASTM D790
Tensile Stress, yield, 5 mm/min
108MPaISO 527
Tensile Stress, break, 5 mm/min
108MPaISO 527
Tensile Strain, yield, 5 mm/min
2%ISO 527
Tensile Strain, break, 5 mm/min
2%ISO 527
Tensile Modulus, 1 mm/min
11000MPaISO 527
Flexural Stress, yield, 2 mm/min
175MPaISO 178
Flexural Stress, break, 2 mm/min
175MPaISO 178
Flexural Strain, break, 2 mm/min
2%ISO 178
Flexural Modulus, 2 mm/min
10000MPaISO 178
Ball Indentation Hardness, H358/30
142MPaISO 2039-1
Hardness, Rockwell R
120-ISO 2039-2
IMPACT2)


Charpy Impact, unnotched, 23°C
40kJ/m²ISO 179/2C
Charpy Impact, unnotched, -30°C
35kJ/m²ISO 179/2C
Izod Impact, unnotched, 23°C
570J/mASTM D4812
Izod Impact, unnotched, -30°C
500J/mASTM D4812
Izod Impact, notched, 23°C
72J/mASTM D256
Izod Impact, notched, 0°C
72J/mASTM D256
Izod Impact, notched, -30°C
65J/mASTM D256
Izod Impact, unnotched 80*10*4 +23°C
37kJ/m²ISO 180/1U
Izod Impact, unnotched 80*10*4 -30°C
37kJ/m²ISO 180/1U
Izod Impact, notched 80*10*4 +23°C
8kJ/m²ISO 180/1A
Izod Impact, notched 80*10*4 0°C
9kJ/m²ISO 180/1A
Izod Impact, notched 80*10*4 -30°C
8kJ/m²ISO 180/1A
Charpy Impact, notched, 23°C
10kJ/m²ISO 179/2C
Charpy Impact, notched, -30°C
10kJ/m²ISO 179/2C
THERMAL2)


Vicat Softening Temp, Rate A/50
217°CASTM D1525
Vicat Softening Temp, Rate B/50
200°CASTM D1525
HDT, 0.45 MPa, 3.2 mm, unannealed
223°CASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed
205°CASTM D648
CTE, -40°C to 40°C, flow
2.E-051/°CISO 11359-2
CTE, -40°C to 40°C, xflow
6.2E-051/°CISO 11359-2
CTE, 23°C to 150°C, flow
2.5E-051/°CISO 11359-2
CTE, 23°C to 150°C, xflow
1.5E-041/°CISO 11359-2
Ball Pressure Test, 125°C +/- 2°C
PASSES-IEC 60695-10-2
Vicat Softening Temp, Rate A/50
220°CISO 306
Vicat Softening Temp, Rate B/50
200°CISO 306
Vicat Softening Temp, Rate B/120
205°CISO 306
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
225°CISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
205°CISO 75/Af
Relative Temp Index, Elec1)140°CUL 746B
Relative Temp Index, Mech w/impact1)125°CUL 746B
Relative Temp Index, Mech w/o impact1)140°CUL 746B
PHYSICAL2)


Specific Gravity
1.56-ASTM D792
Mold Shrinkage, flow, 3.2 mm5)0.28%SABIC method
Mold Shrinkage, xflow, 3.2 mm5)0.57%SABIC method
Filler Content
30%ASTM D229
Melt Flow Rate, 265°C/5.0 kgf
23g/10 minASTM D1238
Density
1.56g/cm³ISO 1183
Water Absorption, (23°C/saturated)
0.23%ISO 62-1
Moisture Absorption (23°C / 50% RH)
0.09%ISO 62
Melt Volume Rate, MVR at 250°C/5.0 kg
16cm³/10 minISO 1133
Melt Viscosity, 260°C, 1500 sec-1
110Pa-sISO 11443
ELECTRICAL2)


Volume Resistivity
1.0E+14Ω.cmASTM D257
Dielectric Strength, in oil, 0.8 mm
32kV/mmASTM D149
Dielectric Strength, in oil, 1.6 mm
22kV/mmASTM D149
Dielectric Strength, in oil, 3.2 mm
18kV/mmASTM D149
Relative Permittivity, 1 MHz
3.8-ASTM D150
Dissipation Factor, 1 MHz
0.14-ASTM D150
Volume Resistivity
1.E+14Ω.cmIEC 60093
Surface Resistivity, ROA
>1.E+15ΩIEC 60093
Dielectric Strength, in oil, 0.8 mm
32kV/mmIEC 60243-1
Dielectric Strength, in oil, 1.6 mm
22kV/mmIEC 60243-1
Dielectric Strength, in oil, 3.2 mm
18kV/mmIEC 60243-1
Relative Permittivity, 1 MHz
3.8-IEC 60250
Dissipation Factor, 1 MHz
0.14-IEC 60250
Comparative Tracking Index (UL) {PLC}
0PLC CodeUL 746A
Comparative Tracking Index4)600VIEC 60112
Hot-Wire Ignition (HWI), PLC 0
≥3mmUL 746A
Hot-Wire Ignition (HWI), PLC 1
≥0.8mmUL 746A
High Amp Arc Ignition (HAI), PLC 0
≥0.8mmUL 746A
INJECTION MOLDING3)


Drying Temperature
110-120°C
Drying Time
2-4Hrs
Maximum Moisture Content
0.02%
Melt Temperature
245-260°C
Nozzle Temperature
230-255°C
Front - Zone 3 Temperature
240-260°C
Middle - Zone 2 Temperature
235-250°C
Rear - Zone 1 Temperature
230-240°C
Hopper Temperature
40-60°C
Mold Temperature
40-100°C


为您推荐
供应商网> 特种塑料> VALOX ENH4560 30%玻璃纤维增强的注塑级树脂
    在线问
    产品参数
    1/2
    ¥98.00 在线咨询
    进店 客服 获取最低报价 拨打电话
    VALOX ENH4560 30%玻璃纤维增强的注塑级树脂
    ¥98.00
    • 采购产品
    • 采购数量
    • 联系电话
    《服务条款》 并允许推荐更多供应商为您服务
    请阅读并同意《服务条款》

    获取成功

    请您注意近期来电

    看这里，您也可以拨打电话咨询产品哦~

    咨询电话：𐁴𐁵𐁴 𐁶𐁷𐁸𐁸 𐁹𐁸𐁹𐁵

    关闭 产品推荐
    知道了