VALOX ENH4550 25%玻璃纤维增强的注塑
¥98.00
VALOX ENH4565 33%的玻璃纤维增强、抗热震
¥98.00
- 商品
- 详情
LNP VERTON WV006 含有长玻璃的聚对苯二甲酸丁二醇酯树脂
- ¥118.00 ≥25千克起批
参数
- 否是否进口
- 中国厂家(产地)
- WV006牌号
广东 东莞
不限
VALOX ENH4550 25%玻璃纤维增强的注塑
¥98.00
VALOX ENH4565 33%的玻璃纤维增强、抗热震
¥98.00
产品详情
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | 1) | |||
| Tensile Stress, break | 187 | MPa | ISO 527 | |
| Tensile Strain, break | 2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 11570 | MPa | ISO 527 | |
| Flexural Stress | 247 | MPa | ISO 178 | |
| Flexural Modulus | 9780 | MPa | ISO 178 | |
| IMPACT | 1) | |||
| Izod Impact, unnotched 80*10*4 +23°C | 56 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 30 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -40°C | 36 | kJ/m² | ISO 180/1A | |
| THERMAL | 1) | |||
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 225 | °C | ISO 75/Af | |
| PHYSICAL | 1) | |||
| Density | 1.54 | g/cm³ | ISO 1183 | |
| INJECTION MOLDING | 2) | |||
| Drying Temperature | 120 | °C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.05 | % | ||
| Melt Temperature | 250-260 | °C | ||
| Front - Zone 3 Temperature | 250-260 | °C | ||
| Middle - Zone 2 Temperature | 240-250 | °C | ||
| Rear - Zone 1 Temperature | 230-245 | °C | ||
| Mold Temperature | 65-120 | °C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-70 | rpm |
为您推荐
-
-
VALOX ENH8560 玻纤填充 ¥98.00
-
LNP STAT-KON Compound VC108. ¥98.00
-
LNP STAT-KON Compound VC112 ¥117.00
-
LNP STAT-KON Compound VC120 ¥78.00
-
LNP STAT-KON Compound VC130 ¥18.00
-
-
-
Xenoy IQNH2900 UL94 V-0无溴阻燃 ¥118.00
-
ULTEM 1000 无定形透明聚醚酰亚胺（PEI）塑料 ¥98.00
-
-
-
ULTEM 1100F ¥128.00
-
ULTEM 2100 10%玻璃纤维填充，标准流量聚醚酰亚胺 ¥128.00
-
-
-
-
在线问
产品参数
- 否
- 中国
- WV006
- 注塑