LNP VERTON RX06422 含有50%长玻璃纤维的尼龙66树脂
- ¥128.00 ≥25千克起批
参数
- 否是否进口
- 中国厂家(产地)
- RX06422牌号
广东 东莞
不限
LNP VERTON RX10409D
¥98.00
产品详情
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| FLAME CHARACTERISTICS | 1) | |||
| UL Yellow Card Link | E45329 - 104432357 | - | - | |
| UL Recognized, 94HB Flame Class Rating | 1) | ≥1.5 | mm | UL 94 |
| UV-light, water exposure/immersion | F1 | - | UL 746C | |
| MECHANICAL | 2) | |||
| Tensile Stress, break | 254 | MPa | ASTM D638 | |
| Tensile Strain, break | 1.9 | % | ASTM D638 | |
| Tensile Modulus, 5 mm/min | 16890 | MPa | ASTM D638 | |
| Flexural Stress | 374 | MPa | ASTM D790 | |
| Flexural Modulus | 14160 | MPa | ASTM D790 | |
| Tensile Stress, break | 256 | MPa | ISO 527 | |
| Tensile Strain, break | 1.9 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 18380 | MPa | ISO 527 | |
| Flexural Stress | 370 | MPa | ISO 178 | |
| Flexural Modulus | 15550 | MPa | ISO 178 | |
| IMPACT | 2) | |||
| Izod Impact, notched, 23°C | 384 | J/m | ASTM D256 | |
| Instrumented Dart Impact Energy @ peak, 23°C | 15 | J | ASTM D3763 | |
| Multiaxial Impact | 15 | J | ISO 6603 | |
| Izod Impact, unnotched 80*10*4 +23°C | 89 | kJ/m² | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -40°C | 38 | kJ/m² | ISO 180/1A | |
| THERMAL | 2) | |||
| HDT, 1.82 MPa, 3.2mm, unannealed | 241 | °C | ASTM D648 | |
| CTE, -40°C to 40°C, flow | 1.85E-05 | 1/°C | ASTM E831 | |
| CTE, -40°C to 40°C, xflow | 6.73E-05 | 1/°C | ASTM E831 | |
| CTE, -40°C to 40°C, flow | 1.86E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 6.73E-05 | 1/°C | ISO 11359-2 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 258 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 253 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 1) | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 1) | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 1) | 110 | °C | UL 746B |
| PHYSICAL | 2) | |||
| Density | 1.58 | g/cm³ | ASTM D792 | |
| Mold Shrinkage, flow, 24 hrs | 4) | 0.3 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 4) | 0.8 | % | ISO 294 |
| Density | 1.58 | g/cm³ | ISO 1183 | |
| ELECTRICAL | 1) | |||
| Hot-Wire Ignition (HWI), PLC 0 | ≥1.5 | mm | UL 746A | |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1.5 | mm | UL 746A | |
| INJECTION MOLDING | 3) | |||
| Drying Temperature | 80 | °C | ||
| Drying Time | 4 | Hrs | ||
| Maximum Moisture Content | 0.15-0.25 | % | ||
| Melt Temperature | 290-305 | °C | ||
| Front - Zone 3 Temperature | 290-300 | °C | ||
| Middle - Zone 2 Temperature | 290-300 | °C | ||
| Rear - Zone 1 Temperature | 280-295 | °C | ||
| Mold Temperature | 95-110 | °C | ||
| Back Pressure | 0.2-0.3 | MPa | ||
| Screw Speed | 30-60 | rpm |
为您推荐
-
VALOX ENH8560 玻纤填充 ¥98.00
-
LNP STAT-KON Compound VC108. ¥98.00
-
LNP STAT-KON Compound VC112 ¥117.00
-
LNP STAT-KON Compound VC120 ¥78.00
-
LNP STAT-KON Compound VC130 ¥18.00
-
-
-
Xenoy IQNH2900 UL94 V-0无溴阻燃 ¥118.00
-
ULTEM 1000 无定形透明聚醚酰亚胺（PEI）塑料 ¥98.00
-
-
-
ULTEM 1100F ¥128.00
在线问
产品参数
- 否
- 中国
- RX06422
- 注塑